30%GFPA6
|
|
版本号： |
A0 |
文件编号： |
PG-06-2009-G60030 |
|
测试项目 |
检测标准 |
单位 |
测试结果 |
|
TEST ITEM |
TEST STANDARDS |
UNIT |
TEST RESULTS |
|
拉伸强度 |
ASTM D638 |
MPa |
172 |
|
Tensile Strength |
|
断裂伸长率 |
ASTM D638 |
% |
3 |
|
Elongation at Break |
|
弯曲强度 |
ASTM D790 |
MPa |
255 |
|
Flexural Strength |
|
弯曲模量 |
ASTM D790 |
MPa |
8500 |
|
Flexural Modulus |
|
悬臂梁缺口冲击强度 |
ASTM D256 |
J/m |
108 |
|
Izod Impact, Notched |
|
热变性温度 |
ASTM D648 |
℃ |
215 |
|
Heat deflection tenperature |
|
燃烧残余 |
|
% |
30 |
|
Buruing Residual |
|
阻燃性能 |
UL 94 |
|
HB |
|
Flame Rating |
|
备注 |
|
|
/ |
|
REMARKS |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
以上数据为实验典型值,仅供参考 | |
改性PA6